1Cr13Al4 alloy is a high resistance electric heating alloy, known
for its excellent corrosion resistance and high-temperature
strength. It has a high electrical resistivity and a low resistance
temperature coefficient. The main components of 1Cr13Al4 include
chromium, aluminum, nickel, etc., which endow the alloy with good
electrical resistivity, high-temperature oxidation resistance, and
corrosion resistance.
The 1Cr13Al4 resistance wire is widely used in industrial heating
applications. They are commonly employed in the manufacturing of
various heating devices, including furnaces, heating tubes, heating
plates, etc. These devices are used to heat various substances such
as liquids, gases, and solids, playing a crucial role in industrial
production.
In the field of metal processing, 1Cr13Al4 resistance wire is often
used as heating elements for heating metal billets for processes
like forging, heat treatment, and shaping. The high-temperature
characteristics of this resistance wire enable rapid and uniform
heating of metals, improving production efficiency and processing
quality.
In the plastic processing industry, 1Cr13Al4 resistance wire is
widely utilized in equipment such as injection molding machines,
extruders, and hot press molding machines. They heat plastic raw
materials to achieve proper flowability, facilitating the molding
and processing of plastic products.
Additionally, 1Cr13Al4 resistance wire is also used in industrial
applications such as drying equipment, drying chambers, and heating
fans. They provide stable heating power and temperature control,
ensuring stability and efficiency in the production process.
In summary, the 1Cr13Al4 resistance wire plays an important role in
industrial heating applications, and its stable performance and
reliability make it an ideal choice for various heating devices.
- Ferrous Chromium Aluminum alloy performance tables
| Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 |
| Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 |
| Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune |
| Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest |
| | | | | | Nb0.5 | Mo1.8-2.2 |
| Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 |
| Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 |
| Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 |
| Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | |
| Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 |
| Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 |
| Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 |
| Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 |
| Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 |
| Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 |
| Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 |
| Continuous Servicetime(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 |
| Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite |
| Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |