1Cr13Al4 alloy is a high resistance electric heating alloy, known
for its excellent corrosion resistance and high-temperature
strength. It has a high electrical resistivity and a low resistance
temperature coefficient. The main components of 1Cr13Al4 include
chromium, aluminum, nickel, etc., which endow the alloy with good
electrical resistivity, high-temperature oxidation resistance, and
corrosion resistance.
The 1Cr13Al4 resistance wire plays an important role in resistance
performance testing. When conducting resistance performance tests,
1Cr13Al4 resistance wire is often used as one of the test samples
to evaluate its resistance characteristics and stability. This type
of testing typically involves measuring the resistance value of the
wire and testing it under different temperatures, humidities, or
other environmental conditions to determine its performance under
various operating conditions.
The resistance characteristics of 1Cr13Al4 resistance wire are
determined based on its material composition and manufacturing
process. Therefore, in resistance performance testing, it is
compared to standard specifications to ensure that it meets the
expected resistance values and performance requirements. Various
measuring devices and instruments such as multimeters, bridges,
etc., may be used during the testing process to ensure accurate
measurement of the resistance wire.
Additionally, durability testing may also be conducted in
resistance performance testing to assess the stability and
durability of 1Cr13Al4 resistance wire under long-term use and
different operating conditions. This type of testing can help
determine the reliability and lifespan of the resistance wire and
provide reference for its performance in practical applications.
Overall, the application of 1Cr13Al4 resistance wire in resistance
performance testing aims to evaluate its resistance characteristics
and stability under different conditions to ensure that it meets
the expected performance requirements and supports its reliability
in various industrial applications.
- Ferrous Chromium Aluminum alloy performance tables
| Alloy Nomenclature Performance | 1Cr13Al4 | 0Cr25Al5 | 0Cr21Al6 | 0Cr23Al5 | 0Cr21Al4 | 0Cr21Al6Nb | 0Cr27Al7Mo2 |
| Main Chemical composition | Cr | 12.0-15.0 | 23.0-26.0 | 19.0-22.0 | 20.5-23.5 | 18.0-21.0 | 21.0-23.0 | 26.5-27.8 |
| Al | 4.0-6.0 | 4.5-6.5 | 5.0-7.0 | 4.2-5.3 | 3.0-4.2 | 5.0-7.0 | 6.0-7.0 |
| Re | opportune | opportune | opportune | opportune | opportune | opportune | opportune |
| Fe | Rest | Rest | Rest | Rest | Rest | Rest | Rest |
| | | | | | Nb0.5 | Mo1.8-2.2 |
| Max. continuous service temp. of element(°C) | 950 | 1250 | 1250 | 1250 | 1100 | 1350 | 1400 |
| Resistivity at 20ºC(μΩ·m) | 1.25 | 1.42 | 1.42 | 1.35 | 1.23 | 1.45 | 1.53 |
| Density(g/cm3) | 7.4 | 7.1 | 7.16 | 7.25 | 7.35 | 7.1 | 7.1 |
| Thermal conductivity(KJ/m·h·ºC) | 52.7 | 46.1 | 63.2 | 60.2 | 46.9 | 46.1 | |
| Coefficient of lines expansion(α×10-6/ºC) | 15.4 | 16 | 14.7 | 15 | 13.5 | 16 | 16 |
| Melting point approx.( ºC) | 1450 | 1500 | 1500 | 1500 | 1500 | 1510 | 1520 |
| Tensile strength(N/mm2) | 580-680 | 630-780 | 630-780 | 630-780 | 600-700 | 650-800 | 680-830 |
| Elongation at rupture(%) | >16 | >12 | >12 | >12 | >12 | >12 | >10 |
| Variation of area(%) | 65-75 | 60-75 | 65-75 | 65-75 | 65-75 | 65-75 | 65-75 |
| Repeat Bending frequency(F/R) | >5 | >5 | >5 | >5 | >5 | >5 | >5 |
| Hardness(H.B.) | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 | 200-260 |
| Continuous Servicetime(Hours/ ºC) | -- | ≥80/1300 | ≥80/1300 | ≥80/1300 | ≥80/1250 | ≥50/1350 | ≥50/1350 |
| Micrographic structure | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite | Ferrite |
| Magnetic properties | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic | Magnetic |